Forsterite L - 514 nm Measured scattering matrix elements as functions of scattering angle (in degrees), corresponding to curves presented in "Retrieving dust grain sizes from photopolarimetry: an experimental approach", Munoz et al. ApJS, 256 (1), 2021, for forsterite L at 514 nm. The experimental errors are also given. F11 is normalized to 1 at a scattering angle of 30 degrees. DATA ARE FREELY AVAILABLE UNDER THE REQUEST OF CITATION OF: Munoz et al. ApJS, 256(1), 2021, AND Munoz et al. JQSRT, 113, 565-574, 2012. theta(deg) F11/F11(30deg) error -F12/F11 error F22/F11 error F33/F11 error F34/F11 error F44/F11 error 3 48.867 10.417 -0.004 0.012 1.019 0.019 ----- ----- ----- ----- ----- ----- 4 27.478 3.047 0.002 0.004 1.018 0.009 ----- ----- ----- ----- ----- ----- 5 15.950 1.396 -0.006 0.008 1.008 0.016 ----- ----- ----- ----- ----- ----- 6 12.422 1.297 -0.001 0.008 0.989 0.011 ----- ----- ----- ----- ----- ----- 7 9.385 0.738 -0.002 0.014 0.971 0.022 ----- ----- ----- ----- ----- ----- 8 7.352 0.443 0.006 0.003 1.049 0.096 ----- ----- ----- ----- ----- ----- 9 5.929 0.354 0.010 0.019 0.988 0.032 ----- ----- ----- ----- ----- ----- 10 5.202 0.224 0.011 0.008 0.971 0.021 ----- ----- ----- ----- ----- ----- 15 2.645 0.100 0.014 0.004 0.919 0.012 ----- ----- ----- ----- ----- ----- 20 1.780 0.021 0.011 0.004 0.913 0.036 ----- ----- ----- ----- ----- ----- 25 1.267 0.023 0.017 0.004 0.877 0.005 ----- ----- ----- ----- ----- ----- 30 1.000 0.010 0.016 0.001 0.851 0.002 ----- ----- ----- ----- ----- ----- 35 0.782 0.025 0.016 0.006 0.817 0.023 ----- ----- ----- ----- ----- ----- 40 0.635 0.011 0.026 0.006 0.780 0.014 ----- ----- ----- ----- ----- ----- 45 0.528 0.007 0.030 0.009 0.742 0.013 ----- ----- ----- ----- ----- ----- 50 0.447 0.015 0.039 0.002 0.694 0.028 ----- ----- ----- ----- ----- ----- 55 0.388 0.010 0.050 0.005 0.660 0.006 ----- ----- ----- ----- ----- ----- 60 0.342 0.009 0.061 0.009 0.616 0.011 ----- ----- ----- ----- ----- ----- 65 0.311 0.007 0.071 0.009 0.563 0.017 ----- ----- ----- ----- ----- ----- 70 0.283 0.015 0.082 0.016 0.527 0.017 ----- ----- ----- ----- ----- ----- 75 0.265 0.008 0.086 0.012 0.503 0.013 ----- ----- ----- ----- ----- ----- 80 0.252 0.008 0.089 0.010 0.464 0.014 ----- ----- ----- ----- ----- ----- 85 0.240 0.009 0.086 0.005 0.421 0.006 ----- ----- ----- ----- ----- ----- 90 0.228 0.007 0.085 0.002 0.403 0.003 ----- ----- ----- ----- ----- ----- 95 0.217 0.008 0.094 0.009 0.381 0.009 ----- ----- ----- ----- ----- ----- 100 0.210 0.008 0.094 0.008 0.366 0.027 ----- ----- ----- ----- ----- ----- 105 0.202 0.007 0.086 0.005 0.336 0.007 ----- ----- ----- ----- ----- ----- 110 0.196 0.008 0.082 0.005 0.320 0.009 ----- ----- ----- ----- ----- ----- 115 0.191 0.009 0.081 0.010 0.322 0.034 ----- ----- ----- ----- ----- ----- 120 0.190 0.008 0.072 0.005 0.301 0.008 ----- ----- ----- ----- ----- ----- 125 0.183 0.008 0.064 0.008 0.305 0.015 ----- ----- ----- ----- ----- ----- 130 0.184 0.008 0.064 0.008 0.301 0.010 ----- ----- ----- ----- ----- ----- 135 0.180 0.008 0.049 0.002 0.291 0.003 ----- ----- ----- ----- ----- ----- 140 0.179 0.001 0.042 0.007 0.294 0.008 ----- ----- ----- ----- ----- ----- 145 0.178 0.005 0.031 0.009 0.293 0.013 ----- ----- ----- ----- ----- ----- 150 0.184 0.008 0.021 0.007 0.304 0.009 ----- ----- ----- ----- ----- ----- 155 0.183 0.004 0.011 0.003 0.307 0.009 ----- ----- ----- ----- ----- ----- 160 0.186 0.005 0.006 0.002 0.326 0.004 ----- ----- ----- ----- ----- ----- 161 0.188 0.006 0.002 0.008 0.325 0.009 ----- ----- ----- ----- ----- ----- 162 0.186 0.005 0.005 0.006 0.343 0.013 ----- ----- ----- ----- ----- ----- 163 0.185 0.009 -0.002 0.004 0.335 0.013 ----- ----- ----- ----- ----- ----- 164 0.187 0.003 0.008 0.002 0.351 0.006 ----- ----- ----- ----- ----- ----- 165 0.191 0.005 -0.001 0.001 0.341 0.007 ----- ----- ----- ----- ----- ----- 166 0.189 0.007 -0.003 0.012 0.352 0.013 ----- ----- ----- ----- ----- ----- 167 0.194 0.003 -0.006 0.003 0.348 0.004 ----- ----- ----- ----- ----- ----- 168 0.195 0.006 -0.010 0.006 0.349 0.008 ----- ----- ----- ----- ----- ----- 169 0.195 0.004 -0.017 0.007 0.366 0.015 ----- ----- ----- ----- ----- ----- 170 0.199 0.003 -0.006 0.003 0.371 0.005 ----- ----- ----- ----- ----- ----- 171 0.202 0.005 -0.004 0.006 0.364 0.010 ----- ----- ----- ----- ----- ----- 172 0.204 0.003 -0.017 0.003 0.376 0.009 ----- ----- ----- ----- ----- ----- 173 0.203 0.001 -0.003 0.007 0.400 0.010 ----- ----- ----- ----- ----- ----- 174 0.217 0.030 -0.014 0.009 0.387 0.012 ----- ----- ----- ----- ----- ----- 175 0.206 0.004 -0.005 0.005 0.404 0.027 ----- ----- ----- ----- ----- ----- 176 0.219 0.002 -0.015 0.009 0.399 0.013 ----- ----- ----- ----- ----- ----- 177 0.227 0.025 -0.001 0.010 0.391 0.027 ----- ----- ----- ----- ----- -----