Forsterite S - 514 nm Measured scattering matrix elements as functions of scattering angle (in degrees), corresponding to curves presented in "Retrieving dust grain sizes from photopolarimetry: an experimental approach", Munoz et al. ApJS, 256 (1), 2021, for forsterite S at 514 nm. The experimental errors are also given. F11 is normalized to 1 at a scattering angle of 30 degrees. DATA ARE FREELY AVAILABLE UNDER THE REQUEST OF CITATION OF: Munoz et al. ApJS, 256(1), 2021, AND Munoz et al. JQSRT, 113, 565-574, 2012. theta(deg) F11/F11(30deg) error -F12/F11 error F22/F11 error F33/F11 error F34/F11 error F44/F11 error 3 25.245 5.944 -0.005 0.004 1.010 0.010 ----- ----- ----- ----- ----- ----- 4 20.805 5.201 -0.005 0.002 0.998 0.007 ----- ----- ----- ----- ----- ----- 5 19.618 1.082 -0.001 0.001 1.009 0.013 ----- ----- ----- ----- ----- ----- 6 15.675 0.648 -0.002 0.002 1.001 0.006 ----- ----- ----- ----- ----- ----- 7 12.575 0.664 0.001 0.000 1.005 0.006 ----- ----- ----- ----- ----- ----- 8 10.162 0.140 0.001 0.003 1.010 0.010 ----- ----- ----- ----- ----- ----- 9 8.257 0.509 0.001 0.002 1.007 0.017 ----- ----- ----- ----- ----- ----- 10 7.390 0.429 0.002 0.001 0.993 0.004 ----- ----- ----- ----- ----- ----- 15 3.479 0.161 0.003 0.001 0.998 0.006 ----- ----- ----- ----- ----- ----- 20 2.045 0.041 0.005 0.001 0.978 0.028 ----- ----- ----- ----- ----- ----- 25 1.371 0.041 0.002 0.001 0.962 0.016 ----- ----- ----- ----- ----- ----- 30 1.000 0.007 0.004 0.001 0.942 0.006 ----- ----- ----- ----- ----- ----- 35 0.763 0.015 0.005 0.001 0.931 0.007 ----- ----- ----- ----- ----- ----- 40 0.596 0.012 0.011 0.002 0.901 0.013 ----- ----- ----- ----- ----- ----- 45 0.479 0.004 0.018 0.002 0.878 0.010 ----- ----- ----- ----- ----- ----- 50 0.392 0.002 0.024 0.002 0.854 0.013 ----- ----- ----- ----- ----- ----- 55 0.329 0.001 0.033 0.002 0.830 0.024 ----- ----- ----- ----- ----- ----- 60 0.279 0.002 0.045 0.001 0.796 0.010 ----- ----- ----- ----- ----- ----- 65 0.240 0.001 0.057 0.004 0.770 0.014 ----- ----- ----- ----- ----- ----- 70 0.212 0.001 0.072 0.004 0.727 0.007 ----- ----- ----- ----- ----- ----- 75 0.187 0.002 0.084 0.001 0.694 0.010 ----- ----- ----- ----- ----- ----- 80 0.169 0.001 0.096 0.005 0.646 0.007 ----- ----- ----- ----- ----- ----- 85 0.153 0.002 0.106 0.004 0.609 0.008 ----- ----- ----- ----- ----- ----- 90 0.141 0.002 0.113 0.002 0.573 0.005 ----- ----- ----- ----- ----- ----- 95 0.130 0.001 0.119 0.001 0.537 0.003 ----- ----- ----- ----- ----- ----- 100 0.120 0.001 0.128 0.005 0.499 0.006 ----- ----- ----- ----- ----- ----- 105 0.114 0.001 0.129 0.004 0.465 0.007 ----- ----- ----- ----- ----- ----- 110 0.107 0.002 0.126 0.003 0.437 0.004 ----- ----- ----- ----- ----- ----- 115 0.102 0.001 0.122 0.003 0.413 0.008 ----- ----- ----- ----- ----- ----- 120 0.098 0.001 0.118 0.004 0.396 0.007 ----- ----- ----- ----- ----- ----- 125 0.093 0.000 0.107 0.002 0.380 0.004 ----- ----- ----- ----- ----- ----- 130 0.091 0.000 0.092 0.002 0.373 0.013 ----- ----- ----- ----- ----- ----- 135 0.089 0.002 0.078 0.001 0.363 0.006 ----- ----- ----- ----- ----- ----- 140 0.087 0.001 0.063 0.002 0.374 0.007 ----- ----- ----- ----- ----- ----- 145 0.086 0.002 0.044 0.005 0.379 0.008 ----- ----- ----- ----- ----- ----- 150 0.087 0.001 0.024 0.001 0.403 0.016 ----- ----- ----- ----- ----- ----- 155 0.086 0.001 0.001 0.005 0.429 0.011 ----- ----- ----- ----- ----- ----- 160 0.088 0.001 -0.024 0.002 0.467 0.010 ----- ----- ----- ----- ----- ----- 161 0.088 0.001 -0.031 0.002 0.471 0.010 ----- ----- ----- ----- ----- ----- 162 0.088 0.002 -0.033 0.001 0.480 0.003 ----- ----- ----- ----- ----- ----- 163 0.089 0.001 -0.036 0.002 0.494 0.005 ----- ----- ----- ----- ----- ----- 164 0.089 0.001 -0.039 0.006 0.512 0.008 ----- ----- ----- ----- ----- ----- 165 0.089 0.001 -0.041 0.001 0.506 0.009 ----- ----- ----- ----- ----- ----- 166 0.090 0.001 -0.042 0.004 0.506 0.011 ----- ----- ----- ----- ----- ----- 167 0.091 0.001 -0.042 0.005 0.512 0.006 ----- ----- ----- ----- ----- ----- 168 0.092 0.001 -0.044 0.007 0.511 0.011 ----- ----- ----- ----- ----- ----- 169 0.096 0.002 -0.041 0.004 0.511 0.015 ----- ----- ----- ----- ----- ----- 170 0.097 0.001 -0.036 0.004 0.504 0.005 ----- ----- ----- ----- ----- ----- 171 0.099 0.001 -0.034 0.004 0.500 0.008 ----- ----- ----- ----- ----- ----- 172 0.104 0.002 -0.030 0.002 0.501 0.017 ----- ----- ----- ----- ----- ----- 173 0.108 0.002 -0.026 0.005 0.478 0.008 ----- ----- ----- ----- ----- ----- 174 0.118 0.010 -0.022 0.003 0.471 0.012 ----- ----- ----- ----- ----- ----- 175 0.114 0.002 -0.015 0.002 0.473 0.006 ----- ----- ----- ----- ----- ----- 176 0.120 0.001 -0.013 0.003 0.463 0.012 ----- ----- ----- ----- ----- ----- 177 0.127 0.004 -0.006 0.006 0.458 0.008 ----- ----- ----- ----- ----- -----