JSC0 (palagonite) - 647 nm Measured scattering matrix elements as functions of scattering angle (in degrees), corresponding to curves for JSC0 (palagonite) at 647 nm presented in "Scattering matrices of Martian dust analogs at 488 nm and 647 nm" D.D. Dabrowska, O. Muñoz, F. Moreno, J.L. Ramos, J. Martínez-Frías, G. Wurm. Icarus, 250, 83-94, 2015. The experimental errors are also given. F11 is normalized to 1 at a scattering angle of 30 degrees. DATA ARE FREELY AVAILABLE UNDER THE REQUEST OF CITATION OF: Dabrowska et al. Icarus, 250, 83-94, 2015, AND Munoz et al. JQSRT, 113, 565-574, 2012. theta(deg) F11/F11(30deg) error -F12/F11 error F22/F11 error F33/F11 error F34/F11 error F44/F11 error 4 33.903 1.812 -0.002 0.001 0.969 0.026 0.990 0.054 -0.029 0.042 0.946 0.197 5 23.710 2.452 0.005 0.005 0.965 0.020 1.046 0.014 0.002 0.020 0.894 0.122 6 17.093 1.542 0.003 0.002 0.950 0.027 1.014 0.017 -0.001 0.013 0.893 0.225 7 12.920 1.009 0.005 0.003 0.939 0.034 0.932 0.019 0.000 0.006 0.884 0.171 8 9.772 0.674 0.004 0.002 0.979 0.036 0.912 0.016 -0.010 0.004 0.896 0.124 9 7.945 0.536 0.005 0.002 0.944 0.042 0.934 0.074 -0.006 0.009 ----- ----- 10 6.595 0.319 0.005 0.000 0.941 0.028 1.011 0.014 -0.010 0.003 0.830 0.101 15 3.276 0.148 0.007 0.002 0.909 0.034 0.987 0.043 -0.003 0.010 0.800 0.194 20 1.963 0.056 0.010 0.003 0.875 0.041 0.948 0.099 -0.012 0.008 0.738 0.089 25 1.344 0.023 0.017 0.001 0.865 0.042 0.836 0.010 0.000 0.004 0.723 0.115 30 1.000 0.000 0.023 0.003 0.856 0.063 0.803 0.025 0.010 0.005 0.745 0.254 35 0.771 0.006 0.033 0.005 0.803 0.048 0.756 0.023 0.021 0.008 0.611 0.092 40 0.632 0.014 0.039 0.003 0.777 0.051 0.693 0.031 0.021 0.003 0.590 0.126 45 0.519 0.006 0.061 0.006 0.718 0.057 0.657 0.010 0.033 0.010 0.590 0.142 50 0.450 0.010 0.068 0.002 0.657 0.040 0.637 0.040 0.063 0.011 0.516 0.177 55 0.397 0.010 0.078 0.007 0.629 0.068 0.575 0.057 0.057 0.032 0.475 0.043 60 0.356 0.010 0.091 0.010 0.586 0.041 0.503 0.009 0.074 0.004 0.400 0.103 65 0.322 0.008 0.110 0.010 0.553 0.024 0.430 0.022 0.063 0.008 0.397 0.187 70 0.303 0.010 0.108 0.011 0.509 0.041 0.390 0.005 0.066 0.009 0.334 0.025 75 0.285 0.008 0.113 0.017 0.464 0.043 0.344 0.021 0.075 0.048 0.316 0.076 80 0.268 0.011 0.135 0.010 0.437 0.023 0.275 0.035 0.079 0.017 0.298 0.093 85 0.259 0.010 0.121 0.029 0.389 0.048 0.216 0.022 0.074 0.016 0.271 0.110 90 0.254 0.011 0.136 0.012 0.364 0.024 0.137 0.004 0.078 0.013 0.207 0.054 95 0.245 0.008 0.127 0.007 0.336 0.040 0.103 0.030 0.109 0.033 0.144 0.033 100 0.242 0.010 0.135 0.017 0.312 0.037 0.034 0.019 0.100 0.022 0.122 0.016 105 0.242 0.017 0.137 0.018 0.287 0.027 -0.014 0.014 0.073 0.018 0.127 0.027 110 0.239 0.021 0.116 0.004 0.275 0.026 -0.040 0.040 0.084 0.017 0.063 0.029 115 0.244 0.015 0.118 0.005 0.278 0.018 -0.086 0.026 0.079 0.019 0.063 0.033 120 0.241 0.018 0.104 0.014 0.264 0.021 -0.118 0.043 0.053 0.018 0.026 0.024 125 0.243 0.012 0.107 0.015 0.274 0.026 -0.169 0.036 0.058 0.011 0.005 0.018 130 0.239 0.017 0.082 0.012 0.243 0.025 -0.182 0.055 0.068 0.023 -0.025 0.027 135 0.245 0.020 0.072 0.010 0.256 0.017 -0.203 0.021 0.028 0.033 -0.055 0.030 140 0.243 0.014 0.041 0.017 0.245 0.023 -0.201 0.106 0.016 0.023 -0.064 0.025 145 0.248 0.024 0.035 0.007 0.270 0.012 -0.259 0.033 0.029 0.040 -0.090 0.024 150 0.249 0.008 0.013 0.052 0.274 0.055 -0.258 0.021 0.027 0.018 -0.133 0.058 155 0.251 0.014 -0.006 0.012 0.285 0.023 -0.290 0.061 0.012 0.012 -0.146 0.025 160 0.264 0.012 0.001 0.001 0.337 0.017 -0.303 0.011 0.010 0.020 -0.149 0.017 165 0.284 0.024 -0.007 0.018 0.359 0.036 -0.306 0.034 -0.010 0.056 -0.164 0.039 170 0.283 0.023 -0.025 0.030 0.356 0.044 -0.328 0.029 -0.017 0.021 -0.176 0.049 171 0.287 0.019 -0.020 0.022 0.364 0.034 -0.339 0.024 0.006 0.029 -0.152 0.021 172 0.284 0.014 -0.013 0.004 0.381 0.029 -0.372 0.198 0.000 0.041 -0.220 0.083 173 0.293 0.034 -0.018 0.014 0.384 0.043 -0.361 0.062 -0.021 0.037 -0.190 0.060 174 0.299 0.016 -0.030 0.019 0.378 0.035 -0.373 0.033 -0.010 0.021 -0.179 0.027 175 0.295 0.018 -0.008 0.011 0.402 0.032 -0.330 0.009 -0.025 0.043 -0.193 0.064 176 0.314 0.035 -0.008 0.038 0.403 0.042 -0.400 0.055 -0.002 0.036 -0.154 0.036